First successful growth of magnetic thin films of meta-stable monoclinic Gd$_{5}$(Si$_{x}$Ge$_{1-x)4}$

ORAL

Abstract

We report on the first successful growth of magnetic thin films of the giant magnetocaloric material Gd$_{5}$(Si$_{x}$Ge$_{1-x})_{4}$. This material has been widely studied for its unusual properties including the coupled magnetic-structural phase transition. We report on the successful growth of films of Gd$_{5}$Si$_{2.09}$Ge$_{1.91}$ that can be used in micro-cooling applications. The film was grown by Pulsed Laser Deposition (PLD) on a (001) silicon wafer deposited at 200$^{\circ}$C from a polycrystalline target. PLD was achieved using a femtosecond laser with a repetition rate of 1kHz, pulse energy of up to 3.5mJ. The deposited film thickness was $\sim$ 400nm measured using Scanning Electron Microscopy and the composition of the film was analyzed using Energy Dispersive Spectroscopy and found to be close to the target composition. Magnetic measurements were carried out in a SQUID magnetometer. Magnetic moment vs. magnetic field measurement confirmed that the film was ferromagnetic at 200K. The transition temperature of the film was measured from magnetic moment vs. temperature measurements using inflection point. Transition temperature was measured at 280K which was close to the 1$^{st}$ order phase transition temperature of bulk material.

–

Authors

  • David Jiles

    Iowa Sate University, Department of Electrical and Computer Engineering, Iowa State University, 1. Department of Electrical and Computer Engineering, Iowa State University 2. Ames Laboratory, US Department of Energy, Iowa State University, Iowa State University, Department of Electrical and Computer Engineering, Iowa State University, Ames, Iowa, Department of Electrical and Computer engineering, Iowa State University, Department of Electrical and Computer engineering, Iowa State University, Iowa, Ames, USA

  • Ravi Hadimani

    Iowa Sate University, Iowa State University, Department of Electrical and Computer engineering, Iowa State University

  • Cajetan Nlebedim

    Iowa State University, Ames Laboratory US DoE, Ames Laboratory, US DOE, Iowa State University, 1. Department of Electrical and Computer Engineering, Iowa State University 2. Ames Laboratory, US Department of Energy, Iowa State University, Ames Laboratory, US DOE, Iowa State University, Ames, Iowa

  • Yevgen Melikhov

    Cardiff University