Reflection from bare and gold coated InP nanowire arrays

POSTER

Abstract

We investigated the spectral and angle resolved reflectance from bare and gold coated (plasmonic) InP nanowire (NW) arrays which were grown by selective area epitaxy. The NWs in the arrays have diameters of 180 nm, heights of ~2 and ~1 micrometers and a pitch of 666 and 500 nm (named areas NWA-1 and NWA-2), respectively. In NWA-2 the NWs additionally possess a 10 nm thick surrounding Al2O3 layer to reduce surface state and metal induced band-bending. A nominally 10 nm thick gold layer was deposited around the NWs in both arrays to study the influence of plasmonic effects. The NW arrays were illuminated with a cw laser at 880 nm for the angle resolved reflectance measurements and with an incandescent light sourced ranged from 500 nm to 1000 nm spectrally resolved experiments. The incident light beams were polarized in p- and s-orientation. The measured spectral and angle resolved reflectance of both uncoated arrays is in very good agreement with finite-difference-time-domain (FDTD) simulations. The experimental results of the gold coated nanowire arrays reveal deviations compared with the FDTD calculations which is tentatively attributed to the granularity of the deposited gold films.

Presenters

  • ChiaWei Tu

    Department of Physics, University of Cincinnati, Cincinnati, OH 45221, U.S.A.

Authors

  • ChiaWei Tu

    Department of Physics, University of Cincinnati, Cincinnati, OH 45221, U.S.A.

  • Qian Gao

    Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Canberra ACT 0200, Australia

  • Hoe Tan

    Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Canberra ACT, 0200, Australia, Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Canberra ACT 0200, Australia, Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Department of Electronic and Materials Engineering, Australian National University

  • Chennupati Jagadish

    Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Canberra ACT, 0200, Australia, Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Canberra ACT 0200, Australia, Department of Electronic Materials Engineering, Research School of Physics and Engineering, Australian National University, Department of Electronic and Materials Engineering, Australian National University

  • Masoud Kaveh-Baghbadorani

    Department of Physics and Astronomy, James Madison University, Harrisonburg, Virginia 22807, U.S.A., Department of Physics and Astronomy, James Madison University

  • Heidrun Schmitzer

    Department of Physics, Xavier University, Cincinnati, OH 45207, Department of Physics, Xavier University, Cincinnati, OH 45207, U.S.A.

  • Martin Fraenzl

    Department of Physics, University of Leipzig, 04103 Leipzig, Germany

  • Hans-Peter Wagner

    Department of Physics, University of Cincinnati, Cincinnati, OH 45221, U.S.A.