Study on bulk nanostructured MnBi permanent magnet prepared by spark plasma sintering

POSTER

Abstract

In this paper, we report on the structure and magnetic properties of bulk nanostructured Mn100-xBix (x = 40, 45, and 52) permanent magnets prepared by spark plasma sintering (SPS) technique. Effect of Mn/Bi ratio on the MnBi low temperature phase (LTP) formation and magnetic properties of the magnets was investigated. Increase of bismuth amount in the synthesized magnets leads to better formation of LTP, resulting in the improvement of both magnetization (at 2 Tesla) and ramanence, but reducing the coercivity of the magnets. Ms increases from 27.87 emu/g for Mn60Bi40 to 45.31 emu/g for Mn48Bi52, while the coercivity decreases from 10.5 kOe to 7.87 kOe at room temperature. For the Mn48Bi52 magnet, TEM observation shows that its microstructure is composed of fine and uniform grains with an average size of 140 nm. The density of the magnet is 8.7g/cm3, which is over 93\% of its theoretical density. Further magnetic measurement at 423 K shows that the Mn60Bi40 magnet possesses a high coercivity of 19 kOe, indicating a strong positive temperature coefficient of coercivity of the bulk nanostructured MnBi permanent magnets.

Authors

  • Dongtao Zhang

    University of Idaho

  • A.N. Behkami

    Kent State University, Reed College, Western Washington University, Washington State University, Department of Physics, University of Idaho, Department of Physics, Whitman College, SciPrint.org, STScI, Physics Dept., Montana State University, Bozeman, MT 59717, Chemistry Dept., Montana State University, Bozeman, MT 59717, Physics Dept., Montana State University, Bozeman, MT 59717; Institut fuer Physik, Technical University Ilmenau, 98693 Ilmenau, Germany, Centre College, Islamic Azad University, Department of Physics, Fars Science and Research Center

  • A.N. Behkami

    Kent State University, Reed College, Western Washington University, Washington State University, Department of Physics, University of Idaho, Department of Physics, Whitman College, SciPrint.org, STScI, Physics Dept., Montana State University, Bozeman, MT 59717, Chemistry Dept., Montana State University, Bozeman, MT 59717, Physics Dept., Montana State University, Bozeman, MT 59717; Institut fuer Physik, Technical University Ilmenau, 98693 Ilmenau, Germany, Centre College, Islamic Azad University, Department of Physics, Fars Science and Research Center

  • A.N. Behkami

    Kent State University, Reed College, Western Washington University, Washington State University, Department of Physics, University of Idaho, Department of Physics, Whitman College, SciPrint.org, STScI, Physics Dept., Montana State University, Bozeman, MT 59717, Chemistry Dept., Montana State University, Bozeman, MT 59717, Physics Dept., Montana State University, Bozeman, MT 59717; Institut fuer Physik, Technical University Ilmenau, 98693 Ilmenau, Germany, Centre College, Islamic Azad University, Department of Physics, Fars Science and Research Center

  • A.N. Behkami

    Kent State University, Reed College, Western Washington University, Washington State University, Department of Physics, University of Idaho, Department of Physics, Whitman College, SciPrint.org, STScI, Physics Dept., Montana State University, Bozeman, MT 59717, Chemistry Dept., Montana State University, Bozeman, MT 59717, Physics Dept., Montana State University, Bozeman, MT 59717; Institut fuer Physik, Technical University Ilmenau, 98693 Ilmenau, Germany, Centre College, Islamic Azad University, Department of Physics, Fars Science and Research Center

  • A.N. Behkami

    Kent State University, Reed College, Western Washington University, Washington State University, Department of Physics, University of Idaho, Department of Physics, Whitman College, SciPrint.org, STScI, Physics Dept., Montana State University, Bozeman, MT 59717, Chemistry Dept., Montana State University, Bozeman, MT 59717, Physics Dept., Montana State University, Bozeman, MT 59717; Institut fuer Physik, Technical University Ilmenau, 98693 Ilmenau, Germany, Centre College, Islamic Azad University, Department of Physics, Fars Science and Research Center