Effect of Polymer Concentration and Cross-linking Density on Microgel Size and Shrinking Capacity

POSTER

Abstract

Hydroxypropylcellulose (HPC) is a polysaccharide with temperature dependent water solubility. HPC chains can be chemically cross linked into stable nanoparticles called microgels. The structure and dynamics of microgels depend on polymer and salt concentration, crosslinking density, and solution temperature. HPC has easily accessible lower critical solution temperature. At T$_{c}$=41$^{\circ}$C, HPC in solution undergoes a reversible transition at which chains form metastable clusters that fall apart when temperature is lowered below T$_{c}$. HPC microgels undergo a similar transition in which, however, microgel clusters stay intact below and above T$_{c}$. In this transition microgels shrink/swell on average by a factor of eight, a property with a potential for application in targeted drug delivery. Dynamic Light Scattering was used to study microgels in thermal equilibrium. Due to a complexity of microgel spectra the line shape analysis algorithm was employed. Comparison of differently synthesized HPC microgels revealed that higher polymer concentration results in smaller microgels with lower shrinking capacity. The effective cross-linking density that yields relatively monodisperse microgels was determined. The angular dependence of scattering demonstrated that microgels are largely spherical particles. Finally, studying microgels at different temperatures allowed to monitor the shrinking/swelling behavior.

Authors

  • Kiril Streletzky

    Cleveland State University, CSU

  • Doug Petkie

    AFRL/RX, AFRL/RX, Systran Systems Inc, UCSD, Los Alamos National Laboratory, Ohio Northern University, BFS, Germany, Florida State University, Monmouth College, Ohio Wesleyan University, Department of Chemical and Biomolecular Engineering, The University of Akron, Physics Department, John Carroll University, Department of Chemistry, Knight Chemical Laboratories, The University of Akron, Australian National University, Miami University, Oxford, OH, University of Cincinnati, University of Findlay, Naval Research Laboratory, Washington, DC 20375, Cleveland State University, Health Sciences Dept, Cleveland State University, Physics Dept, Cleveland State University, Bucknell University, Wright State University, Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright-Patterson AFB, Wright State University, Department of Physics, University of Puerto Rico, Department of Mechanical Engineer, Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright-Patterson AFB and UES, Inc., Department of Environmental Science and Policy, School of Science, Marist College, Poughkeepsie, NY 12601, USA, AFRL/711 HPW, EPA Sustainable Technology Division, University of Akron, Rose-Hulman Institute of Technology, Harvard University, LSU, Ohio University, Wittenberg University, Student

  • John McKenna

    Cleveland State University