Thickness-Controlled Synthesis of Colloidal PbS Nanosheets and Their Thickness-Dependent Energy Gaps.

ORAL

Abstract

Ultrathin colloidal PbS nanosheets are synthesized using organometallic precursors with chloroalkane cosolvents, resulting in tunable thicknesses ranging from 1.2 nm to 4.6 nm. Corresponding photoluminescence peaks are tuned from 1470 nm to 2175 nm. The one-dimensional confinement energy of these quasi-two-dimensional nanosheets is found to be proportional to 1/L instead of 1/L$^2$ (L is the thickness of the nanosheet), which is consistent with results calculated using density functional theory.

–

Authors

  • Zhoufeng Jiang

    Bowling Green State University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Jean-Francois S. VanHuele

    Morehead State University, Indiana University Bloomington, Embry-Riddle Aeronautical University, Bowling Green State University, Psychology Department, Cleveland State University, Physics Dept, Cleveland State University, Brigham Young University

  • Liangfeng Sun

    Bowling Green State University, BGSU