Positron lifetime measurements of origin of photoconductivity in SrTiO3 single crystals

ORAL

Abstract

Positron lifetime measurements were carried out to investigate the origin of two orders of magnitude persistent photoconductivity (PPC) observed in bulk single crystals of strontium titanate (SrTiO3). PPC was realized in annealed samples after exposing them to sub-bandgap light at room temperature. Positron lifetime measurements were performed on as-grown and annealed samples before and after light illumination. They revealed that PPC is attributed to the excitation of an electron from a titanium vacancy related defect into the conduction band. These studies emphasize the importance of positron lifetime spectroscopy in studying complex oxides and revealing new physics and suggest the possibility of developing SrTiO3 for holographic memory. Funding for positron lifetime measurements was provided by the National Science Foundation (DMR1359523 grant).

–

Authors

  • Farida Selim

    Bowling Green State University, Bowling Green State Univ

  • Zachary Richards

    Washington State University, Department of Physics, Bowling Green State University, 104 Overman Hall, OH 43403, USA, Nuclear Radiation Center, PO Box 641300, Washington State University, Pullman, WA 99164-1300, USA, Institute of Nuclear and Physical Engineering, Slovak University of Technology in Bratislava, Ilkovi\v{c}ova 3, 812 19 Bratislava, Slovak Republic, Air Force Institute of Technology, Oak Ridge Institute of Science and Education, Bowling Green State University, Department of Chemistry and Biochemistry, Southern Illinois University, Purdue University, University of Toledo

  • Zachary Richards

    Washington State University, Department of Physics, Bowling Green State University, 104 Overman Hall, OH 43403, USA, Nuclear Radiation Center, PO Box 641300, Washington State University, Pullman, WA 99164-1300, USA, Institute of Nuclear and Physical Engineering, Slovak University of Technology in Bratislava, Ilkovi\v{c}ova 3, 812 19 Bratislava, Slovak Republic, Air Force Institute of Technology, Oak Ridge Institute of Science and Education, Bowling Green State University, Department of Chemistry and Biochemistry, Southern Illinois University, Purdue University, University of Toledo